Fiberon™ PETG-rCF08
Affordable strength and precision from recycled carbon fiber reinforcement
0.45MPa68.6
Modulus
Dry3710 MPa
Modulus
Wet
About PETG-rCF08
Our entry-level composite filament featuring recycled carbon fibers. Inheriting the printability and performance of PETG, while gaining enhanced stiffness from the carbon fiber reinforcement. Print high-speed, moisture-insensitive, and low-creep prototypes with exceptional dimensional accuracy. PETG-rCF08 strikes the perfect balance between affordability and functionality, empowering you to quickly create durable, accurate prototypes.
Application Category
notched
Printer compatibility
270°C
Bed temperature:
60°C
(*) No heated chamber or enclosure needed
Nozzle compatibility
Get inspired by our featured case studies
Our goal is to make materials with a key characteristic - advanced materials that are easy to use for anyone, coming from any industry, without the need of an advanced technological skill set.What is the difference between Fiberon™ PETG-rCF08 and Fiberon™ PET-CF17?
The main differences is in their carbon fiber content and resulting properties. Fiberon™ PETG-rCF08 contains 8% recycled carbon fiber, offering a balanced enhancement of stiffness and strength while maintaining good printability and sustainability. In contrast, Fiberon™ PET-CF17 contains 17% carbon fiber, providing higher levels of stiffness and strength, which may be beneficial for applications requiring greater structural integrity and performance.
What is the percentage of the carbon fiber content in Fiberon™ PETG-rCF08?
It contains 8 wt% carbon fibers.
Do PETG-rCF08 prints need to be annealed? What should be noted when using them?
This material can be used without annealing. Please note that drying at 65°C for 3h before use will help achieve better printing performances.