High-Performance Composite Filaments

Fiberon™ PA6-GF25

Superior thermal and mechanical performance while maintaining excellent printability

Shop now

HDT(°C)
0.45Mpa191

Young's
Modulus
Dry5356 MPa

Young's
Modulus
Wet1793 MPa

Spool info:

1.75mm

500g, 2kg

About PA6-GF25

Fiberon™ PA6-GF25 is a glass fiber reinforced Nylon 6 filament. The material exhibits excellent thermal and mechanical properties without sacrificing the layer adhesion or printability. Fiberon™ PA6-GF25 is strong, durable and features a heat deflection temperature of 191°C. It can be used in applications where stiffness and durability are paramount.

Application Category

Consumer Products

Electronics

Industrial parts

Heat deflection temperature (0.45Mpa)

HDT(°C)191

Young's modulus

Dry5356 MPa

Wet1793 MPa

Tensile strength

dry (x-y)

80.1 MPa

dry (z)

60.7 MPa

wet (x-y)

40.2 Mpa

wet (z)

26.3 MPa

Charpy Impact strength
notched

dry

10.0 kJ/m²

wet

28.0 kJ/m²

Bending modulus

dry (x-y)

4314.2 MPa

wet (x-y)

1448.1 Mpa

(*) all data are from printed specimen

High heat resistance

Dimensionally stable during printing

Download a printer profile

Printer compatibility

Printing temperature:
300°C
Bed temperature:
50°C

(*) No heated chamber or enclosure needed

Nozzle compatibility

Brass nozzle has a lifespan of 9h when printing PA6-GF25. We recommend to use a more durable nozzle.

PA6-GF25

The best thing on the marker for your next awesome project

Shop now

Get inspired by our featured case studies

Our goal is to make materials with a key characteristic - advanced materials that are easy to use for anyone, coming from any industry, without the need of an advanced technological skill set.

June 12, 2024

Recreating Conditions at the Centre of Planets

September 10, 2023

Polymaker & Amesos: Water Pump Mounting Plates for Agricultural Drones

Not sure?
Chat with a specialist

Check material comparison guide

Why should we not exceed 50°C on the bed temperature? Isn't this too low for all other carbon nylon filaments?
Our revolutionary Warp-Free technology has been developed to overcome the barriers of printing difficulties and enhance dimensional stability for Nylon based products. With this innovative solution, our nylon products can be printed at lower bed temperatures without experiencing warpage issues. To maintain the integrity of the Warp-Free technology and prevent warpage, it is advised not to exceed a temperature of 50°Ê when using Fiberon™ PA6-GF25. Higher temperatures can invalidate the Warp-Free technology and accelerate the crystallization speed of polyamide polymers, resulting in potential warping issues. In comparison to competitive products, our filaments exhibit superior dimensional stability, providing an exceptional printing experience.
What is the percentage of the glass fiber content in Fiberon™ PA6-GF25?
It contains 25 wt% carbon fibers.
Do PA6-GF25 prints need annealing? What are the annealing conditions?
We strongly recommend 100°C, 10h annealing to achieve the best performance of the material.